Cements

Cement bases under amalgam or composite fillings, temporary fillings, luting of crownsand bridges, filling of root canals with guttapercha points.

Cement with good mechanical properties, with adjustable working time and consistency.

Cementation of onlays, inlays, fixed restorations and bridges, temporary fillings.

Cement with very fine-grained powder, enabling formation of film up to 25 microns. Allows perfect cavity sealing.

Liners under amalgam or composite fillings, cementation of minor fixed restorations, temporary fillings.

Radiopaque cement, not irritating the pulp, with natural adhesion to hard tissues.

Class I and II restorations not loaded with occlusal forces , class V and III restorations in permanent teeth, class I, II, III, and V laminated restorations in permanent teeth , class I, II, III, and V restorations in deciduous teeth, adhesive liners under composite or amalgam fillings, core build-ups prior to preparation for crowns, inlays or onlays , class I, II, III, and V semipermanent restorations in permanent teeth, fissure sealing.

Radiopaque is glass-ionomer light-cured lining and restorative material with high initial strength. The cement can be finished immediately after light curing, which considerably simplifies and accelerates treatment and minimizes moisture sensitivity of glass-ionomer cement in the initial setting phase. Chemical adhesion to hard dental tissues and long-term fluoride release are retained. In shades similar to VITA™: A2, A3, B3, C3.

Semi-permanent restorations in posterior teeth (class I and II), Class V and III restorations in permanent teeth, Restorations of Class I, II, III, and V in deciduous teeth, Laminated fillings of Class I, II, III, and V in permanent teeth - so-called sandwich technique, Pin retained core build-ups, Adhesive liners under composite or amalgam restorations, A.R.T. technique (Atraumatic Restoration Treatment).

Radiopaque glass-ionomer cement with high mechanical strength and resistance to abrasion, with permanent chemical adhesion to hard dental tissues, fluoride ion release, anti-caries effect and non-sticky condensable consistency. In shades similar to VITA™: A2, A3, B3, C3.

Class V and III fillings in permanent teeth, Class V, III and I laminated fillings in permanent teeth - so called sandwich technique, Class I, II, III and V fillings in deciduous teeth, adhesive liners under composite or amalgam fillings, lost dentine build-ups before preparation for crowns, inlays or onlays or aesthetic veneers, temporary fillings in permanent teeth.

Radiopaque glass-ionomer cement with high mechanical strength and resistance to abrasion, with permanent chemical adhesion to hard dental tissues, fluoride ion release and anti-caries effect. The list of principal features of this product can be complemented by extremely low solubility and disintegration in the oral cavity together with favourable setting time and optimum working time. In shades similar to VITA™: A2, A3, B1, B3, C3.

Cementation of crowns and linear bridges, fixation of orthodontic brackets and retainers, liners under composite fillings.

Glass-ionomer luting cement with low disintegration and low solubility in the oral cavity, high mechanical strength, biological tolerance, anti-caries effect, very low film thickness, excellent handling properties - easy to mix and advantageous course of setting. In shade similar to VITA™: A2.

Temporary fillings, cement bases in cavities close to pulp, permanent root fillings with guttapercha points.

Cement providing good cavity sealing without irritation of adjacent tissues, with analgesic effect.